乐泰408

典型用途：芯吸级别

颜色：清澈

缝隙填充：0.05mm

类型：低气味/低白桦烷氧基

粘度：2600

拉伸剪切强度：5

温度范围：-53°C到71°C

固化速度：初固50秒全固24小时

比重：1.05

adhesive with low odour and non-blooming characteristics.
TYPICAL APPLICATIONS
Bonding applications where vapour control is difficult.
PROPERTIES OF UNCURED MATERIAL
Typical
Value Range
Chemical Type Alkoxy-ethyl
cyanoacrylate
Appearance Water white to straw
coloured liquid
Specific Gravity @ 25°C 1.1
Viscosity @ 25°C, mPa.s (cP)
Brookfield LVF
Spindle #1 @ 60 rpm 7 4 to 10
Flash Point (TCC), °C >82
TYPICAL CURING PERFORMANCE
Under normal conditions, the surface moisture initiates the
hardening process. Although full functional strength is
developed in a relatively short time, curing continues for at
least 24 hours before full chemical/solvent resistance is
developed.
Cure speed vs. substrate
The rate of cure will depend on substrate used. The table
below shows the fixture time achieved on different materials at
22°C , 50% relative humidity. This is defined as the time to
develop a shear strength of 0.1 N/mm² (14.5 psi) tested on
specimens according to ASTM D1002.
Substrate Fixture Time, seconds
Steel (degreased) 30 to 70
Aluminium 5 to 20
Neoprene Nitrile rubber ABS 20 to 60

PVC 20 to 50
Polycarbonate 20 to 60
Phenolic materials 30 to 60
Cure speed vs. bond gap
The rate of cure will depend on the bondline gap. High cure
speed is favoured by thin bond lines. Increasing the bond gap
will slow down the rate of cure.
Cure speed vs. activator
Where cure speed is unacceptably long due to large gaps,
applying activator to the surface will improve cure speed.
However, this can reduce the ultimate strength of the bond,
therefore testing is recommended to confirm effect.

TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Coefficient of thermal expansion, ASTM D696, K-1 80x10-6
Coefficient of thermal conductivity, ASTM C177, W.m-1 K-1 0.1
Glass Transition temperature, ASTM E228, °C
Electrical Properties
Dielectric constant & loss, 25°C, ASTM D150:
Constant Loss
measured at 50Hz: 2.3 1kHz: 2.3 1mHz: 2.3 Volume resistivity, ASTM D257,W.cm: 1 x 1016
Dielectric strength, ASTM D149, kV/mm 25
PERFORMANCE OF CURED MATERIAL
(After 24 hr at 22°C) Typical
Value Range
Shear Strength, ASTM D1002, DIN 53283
Grit Blasted Steel, N/mm² 18 14 to 22
(psi) (2610) (2030 to 3190)
Etched Aluminium, N/mm² 12 9 to 15
(psi) (1740) (1305 to 2175)
ABS, N/mm² >6
(psi) (>870)
PVC, N/mm² 5 2 to 8
(psi) (725) (290 to 1160)
Polycarbonate, N/mm² >3
(psi) (>435)
Phenolic, N/mm² 10 5 to 15
(psi) (145) (700 to 2200)
Neoprene rubber, N/mm² >10
(psi) (>1450)
Nitrile rubber, N/mm² >10
(psi) (>1450)
Tensile Strength, ASTM D2095, DIN 53288
Grit Blasted Steel, N/mm² 17.5 10 to 25
(psi) (2538) (1450 to 3600)

优势方面

我们只提供原装正品汉高乐泰、道康宁、3M、迈图等产品，我们为广大客户朋友提供极具竞争优势的价格。

汉高乐泰是全球胶粘剂技术和品牌市场领导者。

道康宁、迈图是全球硅胶领域的市场领导者。

3M是全球胶带、环氧胶、结构胶等领域的市场领导者。

我们是专业胶粘剂及施胶设备整体解决方案供应商，我们不止卖产品，我们更为客户提供全面而专业的售前指导和售后服务工作，直至广大客户的项目正常运转！

欲知更多产品详情，欢迎咨询深圳市鹏科泰贸易有限公司

网址：http://pengketai.cn.alibaba.com/

电话：0755-86381816

传真：0755-86381822